Effect of Aging on Tensile and Chemical Properties of Polylactic Acid and Polylactic Acid-Like Polymer Materials for Additive Manufacturing.

Additive manufacturing, with its fast development and application of polymeric materials, led to the wide utilization of polylactic acid (PLA) materials. As a biodegradable and biocompatible aliphatic polyester, produced from renewable sources, PLA is widely used in different sectors, from industry to medicine and science. The aim of this research is to determine the differences between two forms of the PLA material, i.e., fused deposition modeling (FDM) printed filament and digital light processing (DLP) printed resin, followed by aging due to environmental and hygiene maintenance conditions for a period of two months. Specimens underwent 3D scanning, tensile testing, and Fourier transform infrared (FTIR) spectrometry to obtain insights into the material changes that occurred. Two-way Analysis of Variance (ANOVA) statistical analysis was subsequently carried out to determine the statistical significance of the determined changes. Significant impairment can be observed in the dimensional accuracies between both materials, whether they are non-aged or aged. The mechanical properties fluctuated for aged FDM specimens: 15% for ultimate tensile stress, 15% for elongation at yield, and 12% for elastic modulus. Regarding the DLP aged specimens, the UTS decreased by 61%, elongation at yield by around 61%, and elastic modulus by 62%. According to the FTIR spectral analysis, the PLA materials degraded, especially in the case of resin specimens. Aging also showed a significant influence on the elastic modulus, ultimate tensile stress, elongation at yield, elongation at break, and toughness of both materials, which was statistically shown by means of a two-way ANOVA test. The data collected in this research give a better understanding of the underlying aging mechanism of PLA materials.

Influence of Aging on the Flexural Strength of PLA and PLA-X 3D-Printed Materials.

The three-point bending test is a valuable method for evaluating the mechanical properties of 3D-printed biomaterials, which can be used in various applications. The use of 3D printing in specimen preparation enables precise control over material composition and microstructure, facilitating the investigation of different printing parameters and advanced materials. The traditional approach to analyzing the mechanical properties of a material using a three-point bending test has the disadvantage that it provides only global information about the material's behavior. This means that it does not provide detailed insight into the local strain distribution within the material. However, the 2D Digital Image Correlation (DIC) method offers additional insight, especially in terms of strain localization. DIC is an optical technique that measures full-field displacements and strains on the surface of a sample. PLA and enhanced PLA-X material were utilized to create three-point bending samples. The aim of this paper was to analyze and compare the influence of aging on the mechanical properties of PLA and enhanced PLA-X materials using three-point bending coupled with the DIC method. The results showed statistically significant differences between the PLA and PLA-X, for both the new and aged materials. The aged PLA samples had the highest average value of maximal force around 68 N, which was an increase of 8.8% compared to the new PLA samples. On the other hand, the aged PLA-X material had an increase of 7.7% in the average maximal force compared to the new PLA-X samples. When comparing the two materials, the PLA samples had higher maximal force values, 6.2% for the new samples, and 7.3% for the aged samples. The DIC results showed that both the new PLA and PLA-X samples endured higher strain values at Points 1 and 2 than the aged ones, except for the aged PLA-X sample at Point 2, where the new sample had higher strain values. However, for the first 5 min of the experiment, both materials exhibited identical behavior, after which point significant differences started to occur for both materials, as well as at Points 1 and 2. A more profound comprehension of the biomechanical characteristics of both PLA and PLA-X material is essential to enhance the knowledge for potential biomedical applications. The DIC method was found to be a powerful tool for analyzing the deformation and failure behavior of samples and for complementing the traditional approach to material testing.

A Comprehensive Mechanical Examination of ABS and ABS-like Polymers Additively Manufactured by Material Extrusion and Vat Photopolymerization Processes.

Additive manufacturing technologies have developed rapidly in recent decades, pushing the limits of known manufacturing processes. The need to study the properties of the different materials used for these processes comprehensively and in detail has become a primary goal in order to get the best out of the manufacturing itself. The widely used thermoplastic polymer material acrylonitrile butadiene styrene (ABS) was selected in the form of both filaments and ABS-like resins to investigate and compare the mechanical properties through a series of different tests. ABS-like resin material is commercially available, but it is not a sufficiently mechanically studied form of the material, which leads to the rather limited literature. Considering that ABS resin is a declared material that behaves like the ABS filament but in a different form, the objective of this study was to compare these two commercially available materials printed with three different 3D printers, namely Fused Deposition Modelling (FDM), Stereolithography (SLA) and Digital Light Processing (DLP). A total of 45 test specimens with geometries and test protocols conforming to the relevant standards were subjected to a series of tensile, three-point bending and compression tests to determine their mechanical properties. Characterization also included evaluation of morphology with 2D and 3D microscopy, dimensional accuracy of 3D scans, and Shore A hardness of each material and 3D printing process. Tensile testing results have shown that FDM toughness is 40% of the value for DLP. FDM elongation at break is 37% of DLP, while ultimate tensile stress for SLA is 27% higher than FDM value. Elastic modulus for FDM and SLA coincide. Flexure testing results indicate that value of DLP flexural modulus is 54% of the FDM value. SLA strain value is 59% of FDM, and DLP ultimate flexure stress is 77% of the value for FDM. Compression test results imply that FDM specimens absorb at least twice as much energy as vat polymerized specimens. Strain at break for SLA is 72% and strain at ultimate stress is 60% of FDM values. FDM yield stress is 32% higher than DLP value. SLA ultimate compressive stress is half of FDM, while value for DLP compressive modulus is 69% of the FDM value. The results obtained are beneficial and give a more comprehensive picture of the behavior of the ABS polymers used in different forms and different AM processes.

The effect of time on mechanical properties of biocompatible photopolymer resins used for fabrication of clear dental aligners.

Clear dental aligners are used for treating orthodontic anomalies (misaligned teeth, inappropriate contact between upper and lower teeth etc.), minor irregularities and bruxism. Using additive manufacturing technologies clear dental aligners are made of biocompatible photopolymer, using a vat photopolymerization technology. One of problems in application is the change of aligner material properties after production, including strength and elongation at failure. This can cause different sequence of tooth displacement which will not correspond to the planned therapy. In this paper three types of material testing are conducted i.e., tensile, compressive and three-point bending testing on specimens of 1 (24 h), 3 (72 h), 5 (120 h) and 7 (168 h) days old. Mechanical properties, such as tensile, compressive and flexural strength and strain at failure are monitored in order to show the effect of time on biocompatible photopolymer resin.